4012G PBT 沙伯基础创新塑料 10%玻璃纤维增强PBT注塑树脂

沙伯基础创新塑料SABIC的VALOX 4012G PBT是一种加10%玻璃纤维增强PBT注塑树脂，具有优异的机械性能,应用程序:连接器,该等级为4012，具有更好的循环时间和延展性

点击下载资料

全国24小时销售热线:

18925783032

获取优惠报价在线咨询产品

沙伯基础创新塑料的VALOX 4012G PBT物性表参数

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min	80	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	80	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D 638
Tensile Modulus, 5 mm/min	4400	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	120	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	120	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	3800	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	80	MPa	ISO 527
Tensile Stress, break, 5 mm/min	80	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3	%	ISO 527
Tensile Strain, break, 5 mm/min	3	%	ISO 527
Tensile Modulus, 1 mm/min	4500	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	125	MPa	ISO 178
Flexural Stress, break, 2 mm/min	120	MPa	ISO 178
Flexural Strain, break, 2 mm/min	5	%	ISO 178
Flexural Modulus, 2 mm/min	3800	MPa	ISO 178
Ball Indentation Hardness, H358/30	110	MPa	ISO 2039-1
Hardness, Rockwell R	120	-	ISO 2039-2
IMPACT
Charpy Impact, unnotched, 23°C	33	kJ/m²	ISO 179/2C
Charpy Impact, unnotched, -30°C	33	kJ/m²	ISO 179/2C
Izod Impact, unnotched, 23°C	380	J/m	ASTM D 4812
Izod Impact, unnotched, -30°C	380	J/m	ASTM D 4812
Izod Impact, notched, 23°C	50	J/m	ASTM D 256
Izod Impact, notched, 0°C	50	J/m	ASTM D 256
Izod Impact, notched, -30°C	50	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	4	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	35	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	30	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 0°C	5	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	7	kJ/m²	ISO 179/1eA
Charpy Impact, notched, 23°C	6	kJ/m²	ISO 179/2C
Charpy -30°C, V-notch Edgew 80104 sp=62mm	6	kJ/m²	ISO 179/1eA
Charpy Impact, notched, -30°C	6	kJ/m²	ISO 179/2C
Charpy 23°C, Unnotch Edgew 80104 sp=62mm	45	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80104 sp=62mm	45	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate A/50	220	°C	ASTM D 1525
Vicat Softening Temp, Rate B/50	205	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	215	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	190	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	8.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	4.63E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, flow	6.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, flow	4.79E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	2.11E-04	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	220	°C	ISO 306
Vicat Softening Temp, Rate B/50	205	°C	ISO 306
Vicat Softening Temp, Rate B/120	200	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	215	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	170	°C	ISO 75/Ae
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	215	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	185	°C	ISO 75/Af
PHYSICAL
Specific Gravity	1.35	-	ASTM D 792
Filler Content	10	%	ASTM D 229
Mold Shrinkage on Tensile Bar, flow	0.6-0.9	%	SABIC method
Mold Shrinkage, flow, 3.2 mm	0.6-1.6	%	SABIC method
Mold Shrinkage on Tensile Bar, xflow	0.7-1	%	SABIC method
Melt Flow Rate, 250°C/1.2 kgf	10	g/10 min	ASTM D 1238
Melt Flow Rate, 266°C/5.0 kgf	90	g/10 min	ASTM D 1238
Density	1.35	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.2	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
Melt Volume Rate, MVR at 250°C/1.2 kg	9	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 250°C/5.0 kg	50	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 265°C/5.0 kg	80	cm³/10 min	ISO 1133
Melt Viscosity, 260°C, 1500 sec-1	110	Pa-s	ISO 11443
ELECTRICAL
Volume Resistivity	>1.E+15	Ohm-cm	ASTM D 257
Dielectric Strength, in oil, 0.8 mm	30	kV/mm	ASTM D 149
Dielectric Strength, in oil, 1.6 mm	23	kV/mm	ASTM D 149
Dielectric Strength, in oil, 3.2 mm	18	kV/mm	ASTM D 149
Relative Permittivity, 1 MHz	3.4	-	ASTM D 150
Dissipation Factor, 1 MHz	0.015	-	ASTM D 150
Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 0.8 mm	30	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	23	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm	18	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	3.4	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.001	-	IEC 60250
Dissipation Factor, 1 MHz	0.015	-	IEC 60250
Comparative Tracking Index	325	V	IEC 60112
Comparative Tracking Index, M	150	V	IEC 60112
Relative Permittivity, 50/60 Hz	3.1	-	IEC 60250
FLAME CHARACTERISTICS
UL Compliant, 94HB Flame Class Rating	1.6	mm	UL 94 by SABIC-IP
Glow Wire Flammability Index 750°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	750	°C	IEC 60695-2-13
Injection Molding
Drying Temperature	110-120	°C
Drying Time	2-4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250-270	°C
Nozzle Temperature	240-260	°C
Front - Zone 3 Temperature	245-265	°C
Middle - Zone 2 Temperature	240-255	°C
Rear - Zone 1 Temperature	230-245	°C
Hopper Temperature	40-60	°C
Mold Temperature	40-100	°C

上一篇：VALOX 4022 PBT 沙伯基础 20%高强度玻璃纤维增强PBT注塑树脂

下一篇：PC/ABS AC25BM 台湾台化TAIRILOY 挤出或吹塑成型级别

产品推荐

新闻&问题

联系方式

18925783032
188078313
188078313@qq.com
东莞市常平镇大京九塑胶城

公司简介

东莞市兴启塑胶原料有限公司是集塑料、化工、为一体的综合性企业，经营泛用塑胶原料、工程塑料和特种工程塑胶原料专业塑胶原料贸易商。公司自成立以来，积极开拓市场，业务辐射全国，并与国内外大型塑胶生产商建立了长期良好的合作关系，主要经营韩国晓星POK、美国伊斯曼PCTG,PETG、台湾长春纯树脂、杜邦、拜耳、沙伯基础创新塑料（原GE）等大型塑胶原料品牌。

产品列表

兴启塑胶

联系方式

东莞市兴启塑胶原料有限公司
手机：18925783032
联系人：李先生
Q Q：188078313
邮箱：188078313@qq.com
地址：东莞市常平镇大京九塑胶城
微信联系

优质产品：PC1414

兴启塑胶是一家专业销售塑胶原料、工程塑料的经营销售商，公司主营PC、ABS、POM、POM、PA66等塑料，型号多样、种类齐全、仓库发货，咨询电话：18925783032。

返回顶部
18925783032
在线咨询
微信二维码

4012G PBT 沙伯基础 创新 塑料 10%玻璃纤维增强PBT注塑树脂

4012G PBT 沙伯基础创新塑料 10%玻璃纤维增强PBT注塑树脂